Synthesis and Optical Studies of InP/ZnSeS/ZnS Semiconductor Quantum Dot

Routh, Tapan (2014) Synthesis and Optical Studies of InP/ZnSeS/ZnS Semiconductor Quantum Dot. Masters thesis, Indian Institute of Science Education and Research Kolkata.

[img] PDF (MS dissertation of Tapan Routh) - Submitted Version
Restricted to Repository staff only

Download (775Kb)

    Abstract

    This dissertation focuses on the synthesis of two different InP base core, core/alloy shell, core/alloy shell/ shell QD. As-prepared QDs were optically studied with absorption, PL spectroscopy and time resolved experiment. Two different colour emissive orange (PL max. 614 nm) and red (PL max. 647 nm) CASS were successfully prepared and optically studied. InP core QD was prepared following gas liquid phase synthesis using Zinc phosphide (instant PH3 gas generation with HCl) as low cost, more stable in air and less toxic phosphorus precursor of InP. As-prepared QDs after complete shelling with ZnSeS and outer most ZnS showed 12 to 18% PL QY. Excited state time constant was measured from time resolved experiment. Their average lifetime was 35 to 40 ns.

    Item Type: Thesis (Masters)
    Additional Information: Supervisor: Dr. Prasun K. Mandal
    Uncontrolled Keywords: InP (core); InP/ZnSeS (CAS); InP/ZnSeS/ZnS; InP/ZnSeS/ZnS (CASS); Optical Studies; Quantum Dot; Semiconductor Quantum Dot; Synthesis
    Subjects: Q Science > QD Chemistry
    Divisions: Department of Chemical Sciences
    Depositing User: IISER Kolkata Librarian
    Date Deposited: 16 Jan 2015 16:31
    Last Modified: 16 Jan 2015 16:32
    URI: http://eprints.iiserkol.ac.in/id/eprint/230

    Actions (login required)

    View Item